ASTM D3410/D3410M : 95

1.1 This test method determines the in-plane compressive properties of polymer matrix composite materials reinforced by high-modulus fibers. The composite material forms are limited to continuous-fiber or discontinuous-fiber reinforced composites for which the elastic properties are specially orthotropic with respect to the test direction. This test procedure introduces the compressive load into the specimen through shear at wedge grip interfaces. This type of load transfer differs from the procedure in Test Method D5467 where compressive load is transmitted into the specimen by subjecting a honeycomb core sandwich beam with thin skins to four-point bending, or Test Method D695 where compressive load is transmitted into the specimen by endloading.

1.2 This procedure is applicable primarily to laminates made from prepreg or similar product forms. Other product forms may require deviations from the test method.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text the inch-pounds units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.

Note 1-Additional procedures for determining compressive properties of resin-matrix composites may be found in Test Methods D5467 and D695.