Standard Specification for Titanium and Titanium Alloy Welded Pipe
1.1 This specification covers the requirements for 33 grades of titanium and titanium alloy welded pipe intended for general corrosion resisting and elevated temperature service as follows:
1.1.1 Grade 1—UNS R50250. Unalloyed titanium, low oxygen,
1.1.2 Grade 2—UNS R50400. Unalloyed titanium, standard oxygen,
1.1.2.1 Grade 2H—UNS R50400. Unalloyed titanium (Grade 2 with 58 ksi (400 MPa) minimum UTS),
1.1.3 Grade 3—UNS R50550. Unalloyed titanium, medium oxygen,
1.1.4 Grade 5—UNS R56400. Titanium alloy (6 % aluminum, 4 % vanadium),
1.1.5 Grade 7—UNS R52400. Unalloyed titanium plus 0.12 to 0.25 % palladium, standard oxygen,
1.1.5.1 Grade 7H—UNS R52400. Unalloyed titanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi (400 MPa) minimum UTS),
1.1.6 Grade 9—UNS R56320. Titanium alloy (3 % aluminum, 2.5 % vanadium),
1.1.7 Grade 11—UNS R52250. Unalloyed titanium plus 0.12 to 0.25 % palladium, low oxygen,
1.1.8 Grade 12—UNS R53400. Titanium alloy (0.3 % molybdenum, 0.8 % nickel),
1.1.9 Grade 13—UNS R53413. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), low oxygen,
1.1.10 Grade 14—UNS R53414. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), standard oxygen,
1.1.11 Grade 15—UNS R53415. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), medium oxygen,
1.1.12 Grade 16—UNS R52402. Unalloyed titanium plus 0.04 to 0.08 % palladium, standard oxygen,
1.1.12.1 Grade 16H—UNS R52402. Unalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi (400 MPa) minimum UTS),
1.1.13 Grade 17—UNS R52252. Unalloyed titanium plus 0.04 to 0.08 % palladium, low oxygen,
1.1.14 Grade 18—UNS R56322. Titanium alloy (3 % aluminum, 2.5 % vanadium plus 0.04 to 0.08 % palladium),
1.1.15 Grade 19—UNS R58640. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum),
1.1.16 Grade 20—UNS R58645. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum) plus 0.04 to 0.08 % palladium,
1.1.17 Grade 21—UNS R58210. Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),
1.1.18 Grade 23—UNS R56407. Titanium alloy (6 % aluminum, 4 % vanadium, extra low interstitial, ELI),
1.1.19 Grade 24—UNS R56405. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.04 to 0.08 % palladium,
1.1.20 Grade 25—UNS R56403. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 to 0.8 % nickel and 0.04 to 0.08 % palladium,
1.1.21 Grade 26—UNS R52404. Unalloyed titanium plus 0.08 to 0.14 % ruthenium,
1.1.21.1 Grade 26H—UNS R52404. Unalloyed titanium plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi (400 MPa) minimum UTS),
1.1.22 Grade 27—UNS R52254. Unalloyed titanium plus 0.08 to 0.14 % ruthenium,
1.1.23 Grade 28—UNS R56323. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,
1.1.24 Grade 29—UNS R56404. Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements (ELI)) plus 0.08 to 0.14 % ruthenium,
1.1.25 Grade 33—UNS R53442. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
1.1.26 Grade 34—UNS R53445. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),
1.1.27 Grade 35—UNS R56340. Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),
1.1.28 Grade 37—UNS R52815. Titanium alloy (1.5 % aluminum),
1.1.29 Grade 38—UNS R54250. Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron), and
1.1.30 Grade 39—UNS R53390. Titanium alloy (0.25 % iron, 0.4 % silicon).
1.2 Pipe 8 in. NPS (nominal pipe size) and larger is most frequently custom made for an order. In such cases, the purchaser carefully should consider the applicability of this specification. Since the pipe is custom made, the purchaser may choose a wall thickness other than those in Table 1 to meet specific operating conditions. The purchaser may also be better served to specify only the portions of this specification that are required to meet the operating conditions (for example, annealing, flattening test, chemistry, properties, etc.).
NPS Desig. | Outside Dia. | Nominal Wall Thickness | ||||||||||||||||
| Schedule 5SA | Schedule 5A | Schedule 10SA | Schedule 10A | Schedule 40S | Schedule 40 | Schedule 80S | Schedule 80 | ||||||||||
in | mm | in | mm | in | mm | in | mm | in | mm | in | mm | in | mm | in | mm | in | mm | |
1/8 | 0.405 | 10.29 | x | x | x | x | 0.049 | 1.24 | 0.049 | 1.24 | 0.068 | 1.73 | 0.068 | 1.73 | 0.095 | 2.41 | 0.095 | 2.41 |
1/4 | 0.540 | 13.72 | x | x | x | x | 0.065 | 1.65 | 0.065 | 1.65 | 0.088 | 2.24 | 0.088 | 2.24 | 0.119 | 3.02 | 0.119 | 3.02 |
3/8 | 0.675 | 17.15 | x | x | x | x | 0.065 | 1.65 | 0.065 | 1.65 | 0.091 | 2.31 | 0.091 | 2.31 | 0.126 | 3.20 | 0.126 | 3.20 |
1/2 | 0.840 | 21.34 | 0.065 | 1.65 | Status : Historical Standard Type: Main Document No: ASTM B862 : 13a Document Year: 2013 Pages: 11 Edition: a
Life CycleHistorical Historical ACTIVE Currently Viewing Historical ASTM B862 : 13a Historical Historical Historical Historical Historical Historical Historical Historical Historical Historical Historical Historical Historical Knowledge Corner Expand Your Knowledge and Unlock Your Learning Potential - Your One-Stop Source for Information! © Copyright 2024 BSB Edge Private Limited. | |||||||||||||